• Place of Origin: Shandong, China (Mainland)

• Shape: Brick

• Material: Alumina Block

• Al2O3 Content (%): 45%

• Refractoriness (Degree): Common (1580°<  Refractoriness<  1770°)

• Model Number: LBR12030203

• Brand Name: LAUREL

• Size: according to customer

• Fuction: coke ovens

• Bulk density: 2.16g/cm3

• Refractoriness: 1770?

• Apparent porodity(%): 20-22

• Thermal expansion at 1000?(%): 0.5

Specifications


Low thermal conductivity
Excellent insulating effect
Good chemical stability
Stable hightemperature performance

1,can make according to designation
2,Good volumn stability

Features

1. Low bulk density, low thermal conductivity, good thermal insulation performance.

2. Refractory category allow direct contact of fire, suitable for various atmosphere

3. Good integrity with furnace lining, long service life, easy operation, could be shaped freely

4. Product specification: standard form, normal standard, shaped and special shaped bricks.

5. Can be used in various kilns because of its cheapness and general tray package. Among all of the refractory materials, it is the most widely used.



Applications

1. Furnaces of metallurgy industry, heat treatment furnace

2. Furnaces of chemical industry and construction industry.

3. Furnace of incineration of garbage, recirculating fluidized bed furnace

Standard sizing: 230 x 114 x 65 mm others up to the client

Item	AL-30	AL-34	AL-38	AL-45	AL-55
AL2O3(min)	30	34	38	45	55
Fe2O3(max)	2.5	2.5	2.0	2.0	2
Refractoriness	1670°C	1710°C	1750°C	1770°C	1770°C
Refractoriness under load,0.2MPa,(°C)	1250	1300	1350	1450	1470
Apparent porosity(%)	22-26	22-26	20-24	20-22	20
Bulk density(g/cm3)	1.9-2.1	1.95-2.1	2.1-2.2	2.15-2.22	2.2-2.35
Cold crushing strength(Mpa)	25	20	30	35	40
Thermal expansion at 1000(%)	0.8	0.6	0.6	0.5	0.4